Europa
EN

USA
UNS

USA
ASTM

China
GB

Russia
GOST

Giappone
JIS

India
IS

Corea
KS

X6CrNiTi18-10

S32100

321

0Cr18Ni11Ti

sus 321

C%

max

Si%

max

Mn%

max

P%

max

S%

Cr%

Ni%

Ti%

max

EN 10088-1:2005

0.08

1.00

2.00

0.045

0.015

17.0-19.0

9.0-12.0

＞5*C＜0.70

±0.005

±0.05

±0.04

±0.005

±0.003

±0.2

±0.15

±0.05

屈服強度
Yield Strength

N/mm2 min

抗拉強度
Tensile Sterength

N/mm2  

伸長率
Elong Ation  

A（%）min

面縮率
Reduction of Arca Z (%)

min

沖擊功
Impace  

 AK(J）

硬度
Hardness

Max HB

190

500-700

40

+AT